Máy thử nghiệm độ biễn dạng vĩnh viễn Model: HZ-7010A

Máy thử nghiệm độ biễn dạng vĩnh viễn

Model:  HZ-7010A

Product Summary:

-          HZ-7010A Distortion of permanent comprssion testing machine. The determination of vulcanized rubber machine applies a constant strain compression deformation of the test method. This test is compressed to the provisions of vulcanized rubber specimens under a high, after a certain temperature and time, or media infiltration, the determination of the rate of the sample compression set.

§  Compression ratio can sample hardness (Shore A-selection)

§  Compression hardness below 50 can choose 40%;

§  Hardness of 50 to 75 compression ratio can choose 30%;

§  Hardness of 75 or more compression ratio can choose 20%.

Main feature:

-          Take the standard test piece, sandwiched between the flat panel of the device in order to screw rotation, compressed to a certain percentage before being placed in a certain temperature of the oven, removed by the prescribed time, remove  the specimen, cooling after 30 minutes, the measured its thickness, with the formula to calculate its degree of compression distortion.

Test Fixture:

-          Compression required smooth surface, its finish is not less than 7

-          Compression plateu deformation in the test should not be proposing to adopt a steel plate, measuring about 75mm, width 50mm, thickness is 10mm.

-          Limiter height of 8 ± 0.02mm, 7 ± 0.02mm, 6 ± 0.02mm.

-          Incubator should have a continuous blast device, box test temperature uniformity. Temperature test area inside the temperature fluctuation range: 100 ℃ The following is ± 1 Centigarde, 100 ~ 200 Centigrade to ± 2 Centigarde.

Sample:

-          Sample is of cylindrical shape with a diameter ofu 10 ± 0.2mm, height of 10 ± 0.2mm.

-          Samples vulcanized with models, the surfaceu should be flat perpendicular and parallel to each other,

Testing Results:

-          Compression ratio K (%) determined by theu formula:

K = Results

-          Compression ratio K (%) determined by the formula:

ho-h2

ho-h

K＝×100

-          ho-compression before the sample height, mm;

-          h1-limiters height, mm;u

-          h2- sample will recovery height compressed, mm.

-          after the test specimen ruptured, the test data will be delete

-          representative of the performance for each sample should not be less than three, whichever is the arithmetic average, to allow deviation as follows: compression set value is less than 10%, the take to allow an absolute deviation of ± 1%, compression set value is greater than 10%, the take to allow the relative deviation of ± 10%. The choice should not be less than the number of samples after the samples of the original  60%.

Technical parameter:

-          Model: HZ-7010A Distortion of permanent comprssion testing machine

-          Rubber specimen: Ф28.68(D)12.7mm

-          Foam plastic: 50*50*25mm

-          Septum thickness: 7.62mm,8.89mm,9.52mm,10.16mm

-          Dimension: 20*12*10cm

Weight: 10kg